PPO/PA NORYL GTX™ GTX8420-1710
48
- Properties:High mobilitydimensional stabilityHigh temperature resistanHydrolysis resistanceFiller: Glass fiber reinf40% filler by weight
- Usages:Electrical applicationsIndustrial machineryParts under the hood of a car
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 10.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.24-0.27 % | |
| 内部方法 | 0.60-0.63 % | ||
| Water absorption rate | ASTM D570 | 0.30 % | |
| ISO 62 | 0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 108 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 13500 Mpa | |
| ISO 527-2/1 | 13900 Mpa | ||
| tensile strength | ASTM D638 | 178 Mpa | |
| ISO 527-2/5 | 198 Mpa | ||
| elongation | ASTM D638 | 2.0 % | |
| ISO 527-2/5 | 2.0 % | ||
| Flexural modulus | ASTM D790 | 11900 Mpa | |
| ISO 178 | 12300 Mpa | ||
| bending strength | ISO 178 | 280 Mpa | |
| ASTM D790 | 249 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | ASTME831 | 1.6E-5到2.0E-5 cm/cm/°C | |
| ASTME831 | 9.0E-5到9.4E-5 cm/cm/°C | ||
| Heat distortion temperature | ASTM D648 | 260 °C | |
| ISO 75-2/Bf | 258 °C | ||
| ASTM D648 | 247 °C | ||
| ISO 75-2/Af | 244 °C | ||
| vicat | ISO 306/B50 | 246 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.