| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.15 g/cm³ |
| Shrinkage rate | | ASTM D995 | 0.50-0.70 % |
| Water absorption rate | | ASTM D570 | 0.20 % |
| melt mass-flow rate | | ASTM D1238 | 15 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 116 R |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 80.0 MPa |
| tensile strength | | ASTM D638 | 56.0 MPa |
| elongation at break | | ASTM D638 | 60 % |
| Flexural modulus | | ASTM D790 | 2400 MPa |
| Impact strength of cantilever beam gap | | ASTM D256 | 540 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 350 J/m |
| Flame retardant performance | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL -94 | HB 1.60mm |
| UL flame retardant rating | | UL -94 | HB 3.20mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+16 Ω.cm |
| Surface Resistivity | | ASTM D257 | 1E+14 Ω.cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 115 °C |
| Heat distortion temperature | | ASTM D648 | 126 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.