LCP E6808-UHF-BZ TAIWAN POLYPLASTICS

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedLow warpage

Supplier(0)

Product Description

Certificates(0)

Datasheet

Product Description

Properties:

Glass fiber reinforced | Low warpage

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	6.40 mm	ASTM D256	350	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.30 mm	UL 94	V-0
Extreme Oxygen Index		ISO 527-1	48	%
Solder resistance		Internal Method	290	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638	100	Mpa
elongation	Break	ASTM D638	5.0	%
Bending modulus	23°C	ASTM D790	9400	Mpa
bending strength	23°C	ASTM D790	120	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			130	°C
drying time			4.0 to 24	hr
Temperature at the rear of the barrel			280 to 320	°C
Temperature in the middle of the barrel			320 to 340	°C
Temperature at the front of the material cylinder			340 to 360	°C
Spray nozzle temperature			340 to 360	°C
Processing (melt) temperature			350	°C
Mold temperature			40 to 160	°C
Injection pressure			80.0 to 160	Mpa
Injection speed			中等偏快
Maintain pressure			20.0 to 40.0	Mpa
Back pressure			1.00 to 5.00	Mpa
Screw speed			50 to 100	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	240	°C
Linear coefficient of thermal expansion	Flow : 150°C	Internal Method	1.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 150°C	Internal Method	6.2E-5	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	Internal Method	1.0	%
Shrinkage rate	Shrinkage rate	Flow	Internal Method	0.22	%
Water absorption rate	Saturation	ASTM D570	0.020	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257	1.0E+15	ohms·cm
Dielectric constant	1 MHz	ASTM D150	3.80
Dielectric constant	Dielectric constant	1.00 GHz	ASTM D150	3.40
Dissipation factor	1 MHz	ASTM D150	0.033
Dissipation factor	Dissipation factor	1.00 GHz	ASTM D150	4.0E-3
Arc resistance		ASTM D495	132	sec
Compared to the anti leakage trace index		IEC 60112	PLC 3
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	96

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.