Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTMD1238 | 0.90 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D-2457 | 63 |
| Haze ratio | | ASTM D-1003 | 12 % |
| gloss | | ASTMD2457 | 63 |
| Haze ratio | | ASTMD1003 | 12 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D-792 | 0.919 g/m3 |
| melt mass-flow rate | | ASTM D-1238 | 0.9 g/10min |
| film thickness | | | 50.8 um |
| Other performance | Test Condition | Test Method | Test Result |
|---|
| Movie Piercing Resistance | | Internal Method | 16.6 J/cm³ |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tangent modulus (MD) | | ASTM D-882 | 168 Mpa |
| Tangent modulus (TD) | | ASTM D-882 | 238 Mpa |
| Tensile yield strength (MD) | | ASTM D-882 | 14.2 Mpa |
| Tensile yield strength (TD) | | ASTM D-882 | 14.6 Mpa |
| Tensile fracture strength (TD) | | ASTM D-882 | 39.2 Mpa |
| Tensile strength at break (MD) | | ASTM D-882 | 48.8 Mpa |
| Tensile elongation at break (TD) | | ASTM D-882 | 740 % |
| Tensile elongation at break (MD) | | ASTM D-882 | 620 % |
| Falling hammer impact | | ASTM D-1709A | 300 g |
| Elmendorf Tear Strength (TD) | | ASTM D-1922 | 1000 g |
| Elmendorf Tear Strength (MD) | | ASTM D-1922 | 720 g |
| film | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTMD882 | 14.2 Mpa |
| tensile strength | | ASTMD882 | 14.6 Mpa |
| tensile strength | | ASTMD882 | 48.8 Mpa |
| tensile strength | | ASTMD882 | 39.2 Mpa |
| elongation | | ASTMD882 | 620 % |
| elongation | | ASTMD882 | 740 % |
| Falling hammer impact | | ASTMD1709A | 300 g |
| Elmondov tear strength | | ASTMD1922 | 720 g |
| Elmondov tear strength | | ASTMD1922 | 1000 g |
| Film thickness - tested | | | 51 µm |
| Membrane puncture resistance | | 内部方法 | 16.6 J/cm³ |
| Secant modulus | | ASTMD882 | 168 Mpa |
| Secant modulus | | ASTMD882 | 238 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | Internal Method | 120 °C |
| vicat | | ASTM D-1525 | 107 °C |
| vicat | | ASTMD1525 | 107 °C |
| | 内部方法 | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.