Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 2.4 g/10min |
| Melt volume flow rate | | ISO 1133 | 1.90 cm3/10min |
| Shrinkage rate | | ISO 294-4 | 2.0 % |
| Shrinkage rate | | ISO 294-4 | 1.8 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 94 |
| Rockwell hardness | | ISO 2039-2 | 122 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | <100 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| Flammability level | | IEC 60695-11-10,-20 | HB |
| FMVSS flammability | | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| Emission | | VDA275 | <8.00 mg/kg |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 3100 Mpa |
| tensile strength | | ISO 527-2 | 72.0 Mpa |
| Tensile strain | | ISO 527-2 | 22 % |
| Nominal tensile fracture strain | | ISO 527-2 | 40 % |
| Flexural modulus | | ISO 178 | 2900 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| AnnealingTime-Optional | | | 30.0 min/mm |
| Heat distortion temperature | | ISO 75-2/B | 165 °C |
| Heat distortion temperature | | ISO 75-2/A | 97.0 °C |
| melting temperature | | ISO 11357-3 | 178 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1E-04 cm/cm/°C |
| AnnealingTemperature | | | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.