Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | 内部方法 | 0.40to0.74 % |
| Shrinkage rate | | 内部方法 | 0.40to0.70 % |
| Water absorption rate | | ISO 62 | 0.20 % |
| Water absorption rate | | ISO 62 | 0.60 % |
| density | | ISO 1183 | 1.18to1.20 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Limiting Oxygen Index | | ASTM D2863 | 32 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | | ASTM D256 | 450 J/m |
| Charpy Notched Impact Strength | | ISO 179/1eA | 20 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 85.0 MPa |
| Tensile modulus | | ISO 527-2/1 | 2500 MPa |
| tensile strength | Yield | ISO 527-2/50 | 65.0 MPa |
| tensile strength | Break | ISO 527-2/50 | 50.0 MPa |
| Tensile strain | Break | ISO 527-2/50 | 45 % |
| Flexural modulus | | ISO 178 | 2450 MPa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| dielectric strength | | IEC 60243-1 | 22 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | 110 °C |
| Continuous use temperature | | IEC 60216 | 60.0 °C |
| ball-indentation hardness | | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 7E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.