PPO(PPE)

PPO(PPE) LUVOCOM® 1700-1401 LEHVOSS Group

Properties:
Filler glass carbon fiber reinforced material
Usages:
Applications in the automotive field textile applications cams business equipment and engineering accessories
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	7.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1fU	18 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1fU	16 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Bending strain		ISO 178	2.0 %
bending strength		ISO 178	125 MPa
Bending modulus		ISO 178	8000 MPa
Tensile strain	Yield	ISO 527-2	1.5 %
tensile strength	Break	ISO 527-2	100 MPa
Tensile modulus		ISO 527-2	7500 MPa

thermal performance	Test Condition	Test Method	Test Result
thermal conductivity		DIN 52612	0.33 W/m/K
Linear coefficient of thermal expansion	MD	DIN 53752	5E-05 cm/cm/°C
Continuous use temperature		UL 746B	110 °C
Vicat softening temperature		ISO 306/A	145 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	23°C,24hr		<0.060 %
Shrinkage rate		DIN 16901	0.20to0.50 %
melt mass-flow rate	300°C/5.0kg	ISO 1133	15 g/10min
density		ISO 1183	1.16 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
insulation resistance		IEC 60167	<1.0E+4 ohms
Surface resistivity		IEC 60093	<1.0E+3 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.