PA6 AL27EN GRUPA AZOTY GERMANY
24
CompareTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| notes | 能替代产品：B3S B30S | ||
| characteristic | 良好的脱模性和尺寸稳定性.快速成型.在同类产品性能最佳 | ||
| Color | 本色 | ||
| purpose | 注塑级尼龙 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 6.4 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 50 % | |
| tensile strength | ASTM D638/ISO 527 | 73 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 160 | |
| Flexural modulus | ASTM D790/ISO 178 | 2700 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 105 kg/cm²(MPa)[Lb/in²] |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.140.65-1.2 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 16 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 3.3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-2 | |
| Heat distortion temperature | ASTM D648/ISO 75 | 70 ℃（℉） | |
| melting temperature | 220 ℃（℉） |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.