PA/ABS Terblend®N N NM-19 BASF USA
177
- Properties:UV resistanceEasy to processHigh mobilityHigh impact resistance
- Usages:Automotive sectorAutomotive interior partssporting goodsLow temperature applicati
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 240°C/10.0kg | ISO1133 | 25.0 | cm3/10min |
| Shrinkage rate | ISO294-4 | 0.80 | % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 1.1 | % |
| Melt Volume-Flow Rate (MVR) | 240°C/10.0kg | ISO1133 | 30.0 | cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 1.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 2000 | Mpa | |
| ISO527-2 | 1600 | Mpa | ||
| tensile strength | 屈服,23°C | ISO527-2 | 35.0 | Mpa |
| elongation | 屈服,23°C | ISO527-2 | 3.4 | % |
| Bending modulus | ISO178 | 1500 | Mpa | |
| bending strength | ISO178 | 50.0 | Mpa | |
| tensile strength | 屈服,23°C | ISO527-2 | 43.0 | Mpa |
| elongation | 屈服,23°C | ISO527-2 | 3.5 | % |
| Bending modulus | ISO178 | 1800 | Mpa | |
| bending strength | ISO178 | 62.0 | Mpa | |
| Rockwell hardness | R级 | ISO2039-2 | 103 | |
| Ball pressure hardness | ISO2039-1 | 86.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Annealed | ISO75-2/B | 85.0 | °C |
| 0.45MPa,退火 | ISO75-2/B | 80.0 | °C | |
| 1.8MPa,退火 | ISO75-2/A | 58.0 | °C | |
| vicat softening point | -- | ISO306/A50 | 165 | °C |
| -- | ISO306/B50 | 91.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Hot deformation temperature | 1.8MPa,退火 | ISO75-2/A | 65.0 | °C |
| vicat softening point | -- | ISO306/A50 | 160 | °C |
| -- | ISO306/B50 | 102 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Relative permittivity | 1MHz | IEC60250 | 2.90 | |
| Dissipation factor | 1MHz | IEC60250 | 0.015 | |
| Leakage Trace Index | IEC60112 | 600 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation MD | 断裂 | ISO527-3 | >50 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.