Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 22 g/10min |
| Shrinkage rate | | 内部方法 | 0.40-0.60 % |
| Water absorption rate | | ASTM D570 | 0.11 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | 5VB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTM D790 | 2620 Mpa |
| bending strength | | ASTM D790 | 94.0 Mpa |
| Tensile modulus | | ASTM D638 | 3000 Mpa |
| tensile strength | | ASTM D638 | 63.0 Mpa |
| tensile strength | | ASTM D638 | 49.0 Mpa |
| elongation | | ASTM D638 | 4.0 % |
| elongation | | ASTM D638 | 80 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact | | ASTM D3763 | 51.0 J |
| Dart impact | | ASTM D3763 | 51.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | | IEC 60243-1 | 17 KV/mm |
| relative permittivity | | IEC 60250 | 2.70 |
| relative permittivity | | IEC 60250 | 2.70 |
| relative permittivity | | IEC 60250 | 2.70 |
| Dissipation Factor | | IEC 60250 | 4E-03 |
| Dissipation Factor | | IEC 60250 | 4E-03 |
| Dissipation Factor | | IEC 60250 | 6E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 98.0 °C |
| Heat distortion temperature | | ASTM D648 | 83.0 °C |
| Heat distortion temperature | | ASTM D648 | 90.0 °C |
| vicat | | ASTM D15255 | 99.0 °C |
| RTI Elec | | UL 746 | 80.0 °C |
| RTI Imp | | UL 746 | 70.0 °C |
| RTI Str | | UL 746 | 80.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.