HIPS HP8250 BK FCFC TAIWAN

Form：Granules | Grade：Injection grade

Properties:

High impact resistanceHigh impact resistanceFor general molding purpo

Typical Applications:

machineMechanical componentsToyFoamstructureHome appliance shellTV casingTerminal housingComputer host panel

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	machine \| Mechanical components \| Toy \| Foam \| structure \| Home appliance shell \| TV casing \| Terminal housing \| Computer host panel
Properties:	High impact resistance \| High impact resistance \| For general molding purpo

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Residual monomer			700	ppm max
melt mass-flow rate	200℃×5kg(49N)	ASTM D-1238(ISO 1133)	5.5	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	23℃,6.4mm	ASTM D-256(ISO R180)	11.0(108)	kg.cm/cm(Jm)
Bending modulus	23℃	ASTM D-790(ISO 178)	2.3(2260)	kg/cm
bending strength	23℃	ASTM D-790(ISO 178)	440(43)	kg/cm
elongation	23℃	ASTM D-638(ISO 527)	40	%
Tensile modulus	23℃	ASTM D-638(ISO 527)	1.5(1470)	kg/cm
tensile strength	23℃	ASTM D-638(ISO 527)	220(22)	kg/cm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	Annealed 80℃×2Hr,3.2mm	ASTM D-1525 D-648(ISO 306B 75/A)	88	°C
Vicat softening temperature	Annealed 80℃×2Hr,3.2mm	ASTM D-1525 D-648(ISO 306B 75/A)	95	°C
Combustibility	FILE NO.E117170	UL 94	1/16"HB NC

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.