Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 0.902 g/cm³ |
| density | | ISO 1183 | 0.902 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 1.3 g/10min |
| melt mass-flow rate | | ISO 1133 | 1.3 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 75 |
| Rockwell hardness | | ISO 2039-2 | 79 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | Injection | ISO 13468-1 | 13 % |
| Haze ratio | | ASTM D1003 | 24 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 25.0 MPa |
| tensile strength | | ISO 527-2 | 31.0 MPa |
| elongation | | ASTM D638 | 13 % |
| Tensile strain | | ISO 527-2 | 13 % |
| Flexural modulus | Injection | ASTM D790 | 800 MPa |
| Flexural modulus | Injection | ISO 178 | 950 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 400 J/m |
| Impact strength of cantilever beam gap | | ISO 180 | 19 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ASTM D648 | 80.0 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/B | 75.0 °C |
| Hot deformation temperature (HDT) | | ASTM D648 | 48.0 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 48.0 °C |
| vicat | | ASTM D15253 | 130 °C |
| vicat | | ISO 306/A | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.