PC IUPILON™ S-2000UR MITSUBISHI GAS SHANGHAI
38
- Properties:Medium viscosityheat-resisting
- Usages:Electronic and electrical componentsAutomotive Applications
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO1183 | 1.20 g/cm³ | |
| melt mass-flow rate | ISO1133 | 10 g/10min | |
| Melt volume flow rate | ISO1133 | 9.00 cm3/10min | |
| Shrinkage rate | 0.50到0.70 % | ||
| 0.50到0.70 % | |||
| Water absorption rate | ISO62 | 0.24 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | ISO527-2 | 61.0 Mpa | |
| Tensile strain | ISO527-2 | 5.6 % | |
| Nominal tensile fracture strain | ISO527-2 | 110 % | |
| Flexural modulus | ISO178 | 2300 Mpa | |
| Bending stress | ISO178 | 93.0 Mpa | |
| Tensile modulus | ISO527-2 | 2400 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO179 | 76 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179 | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 6E+15 ohms | |
| Volume resistivity | IEC60093 | 3E+16 ohms·cm | |
| dielectric strength | IEC60243-1 | 31 KV/mm | |
| IEC60243-1 | 18 KV/mm | ||
| Relative Permittivity | IEC60250 | 3.10 | |
| IEC60250 | 3.10 | ||
| Dissipation Factor | IEC60250 | 6E-04 | |
| IEC60250 | 9E-03 | ||
| Compared to the Leakage Tracking Index (CTI) | UL746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 0.45MPa, Not annealed | ISO75-2/B | 143 °C | |
| 1.8MPa, Not annealed | ISO75-2/A | 129 °C | |
| Linear thermal expansion coefficient | ISO11359-2 | 6.5E-05 cm/cm/°C | |
| ISO11359-2 | 6.6E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.