Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt finger | | ISO 1133 | 17 g/10 min |
| Shrinkage rate | | ISO 294-4 | 0.5-0.7 % |
| Shrinkage rate | | ISO 294-4 | 0.5-0.7 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| proportion | | ASTM D792 | 1.19 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-1 无 |
| UL flame retardant rating | | UL 94 | V-0 无 |
| UL flame retardant rating | | UL 94 | 5VB 无 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO 62 | 0.22 % |
| Tensile modulus | | ISO 527-2/1 | 2350 Mpa |
| tensile yield strength | | ISO 527-2/50 | 60 Mpa |
| elongation at break | | ISO 527-2/50 | 100 % |
| elongation at break | | ISO 527-2/50 | 50 % |
| Flexural modulus | | ISO 178 | 2300 Mpa |
| bending strength | | ISO 178 | 95 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1000000000000000 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| tensile breaking strength | | ISO 527-2/5 | 50 Mpa |
| elongation at yield | | ISO 527-2/50 | 7 % |
| | ISO 75-2/B | 125 °C |
| | ISO 75-2/A | 112 °C |
| Linear expansion coefficient | | ASTM D696 | 0.000070 cm/cm/°C |
| Linear expansion coefficient | | ASTM D696 | 0.000070 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.