PMMA

PMMA ACRYPET™ VH001 MITSUBISHI SAUDI

Properties:
UV resistancestandardHigh temperature resistanWeather resistancetransparent
Usages:
Household appliancesHousehold appliancesCastersOptical level
Compare View Prices

Technical Data Sheet

machinability	Test Condition	Test Method	Test Result
Shrinkage rate		ASTM D-955	0.2-0.6 %
Shrinkage rate	Shrinkage rate		ASTM D-955	MF｜0.2-0.6 %

Basic Performance	Test Condition	Test Method	Test Result
melt mass-flow rate	230℃,3.8kg	ASTM D-1238	2.5 g/10min
melt mass-flow rate	melt mass-flow rate	230℃,3.8kg	ASTM D-1238	MF｜2.0 g/10min
Water absorption rate	24hr	ASTM D-570	0.3 %
Water absorption rate	Water absorption rate	24hr	ASTM D-570	MF｜0.3 %

mechanical properties	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D-785	MF｜100 M Scale
Rockwell hardness	Rockwell hardness		ASTM D-785	95 M Scale
Elongation at Break		ASTM D-638	MF｜5 %
Elongation at Break	Elongation at Break		ASTM D-638	5 %
Impact strength of cantilever beam gap	1/4″付	ASTM D-255	MF｜1.7 kg·cm/cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	1/4″付	ASTM D-255	1.6 kg·cm/cm
tensile strength		ASTM D-638	MF｜740 kg/cm2
tensile strength	tensile strength		ASTM D-638	730 kg/cm2
compressive strength		ASTM D-695	MF｜1100 kg/cm2
compressive strength	compressive strength		ASTM D-695	1100 kg/cm2
Bending modulus	1/4″棒	ASTM D-790	MF｜3.2×104 kg/cm2
Bending modulus	Bending modulus	1/4″棒	ASTM D-790	3.1×104 kg/cm2
bending strength	1/4″棒	ASTM D-790	MF｜1100 kg/cm2
bending strength	bending strength	1/4″棒	ASTM D-790	1100 kg/cm2

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	18.56kg/cm2	ASTM D-648	MF｜102 °C
Hot deformation temperature	Hot deformation temperature	18.56kg/cm2	ASTM D-648	92 °C
Linear coefficient of thermal expansion		ASTM D-696	6×10-5 cm/cm/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ASTM D-696	MF｜6×10-5 cm/cm/℃
specific heat			0.35 cal/g/℃
specific heat	specific heat			MF｜0.35 cal/g/℃
thermal conductivity		ASTM C-177	5×10-4 Cal/s/cm/℃
thermal conductivity	thermal conductivity		ASTM C-177	MF｜5×10-4 Cal/s/cm/℃
Vicat softening temperature	1kg	ASTM D-1525	107 °C
Vicat softening temperature	Vicat softening temperature	1kg	ASTM D-1525	MF｜116 °C

Physical properties	Test Condition	Test Method	Test Result
Refractive index		ASTM D-542	1.49
Refractive index	Refractive index		ASTM D-542	MF｜1.49
Transmittance rate	3.2mm	ASTM D-1003	93 %
Transmittance rate	Transmittance rate	3.2mm	ASTM D-1003	MF｜93 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		JIS K-6911	>1015
Volume resistivity	Volume resistivity		JIS K-6911	MF｜>1015
Dielectric loss	60Hz，Tangent		0.05
Dielectric loss	Dielectric loss	60Hz，Tangent		MF｜0.05
Volume resistivity		JIS K-6911	>1016
Dielectric strength			20
Dielectric constant	60Hz		MF｜3.7
Volume resistivity		JIS K-6911	MF｜>1016
Dielectric constant	60Hz		3.7
Arc resistance		JIS K-6911	MF｜没有痕迹
Arc resistance	Arc resistance		JIS K-6911	没有痕迹
Dielectric strength			MF｜20

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PMMA ACRYPET™ VH001 MITSUBISHI SAUDI

Technical Data Sheet