Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.29 g/cm³ |
| melt mass-flow rate | | ASTM D1238 | 10 g/10min |
| melt mass-flow rate | | ASTM D1238 | 13 g/10min |
| Shrinkage rate | | ASTM D955 | 0.60to0.95 % |
| Shrinkage rate | | ASTM D955 | 0.50to0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-1 |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | 5VA |
| Burning wire flammability index | | IEC 60695-2-12 | 825 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2330 MPa |
| tensile strength | | ASTM D638 | 53.0 MPa |
| tensile strength | | ASTM D638 | 45.0 MPa |
| elongation | | ASTM D638 | 4.1 % |
| elongation | | ASTM D638 | 150 % |
| Flexural modulus | | ASTM D790 | 2270 MPa |
| bending strength | | ASTM D790 | 82.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 750 J/m |
| Dart impact | | ASTM D3763 | 49.0 J |
| Dart impact | | ASTM D3763 | 62.0 J |
| Dart impact | | ASTM D3763 | 45.0 J |
| Dart impact | | ASTM D3763 | 60.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 5.2E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+18 ohms·cm |
| dielectric strength | | IEC 60243-1 | 31 kV/mm |
| dielectric strength | | IEC 60243-1 | 18 kV/mm |
| relative permittivity | | IEC 60250 | 3.28 |
| relative permittivity | | IEC 60250 | 3.12 |
| Dissipation Factor | | IEC 60250 | 3E-03 |
| Dissipation Factor | | IEC 60250 | 0.020 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 79.0 °C |
| vicat | | ASTM D15256 | 140 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 7.4E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 109 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.