ABS POLYLAC® PA-707K
334
- Properties:High rigidityHigh gloss
- Usages:Office suppliesLighting fixturesElectronic fieldElectrical field
- Certificates:ULMSDSSGS
Compare
View PricesTechnical Data Sheet
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 高光泽性 高刚性 |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D-1238 | 1.9 g/10min | |
| ISO 1133 | 23 g/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 14(2.6) kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | ASTM D638/ISO 527 | 500（7.090） kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 15 % | |
| Rockwell hardness | ASTM D785 | R-116 | |
| Flexural modulus | ASTM D790/ISO 178 | 29000（41000） kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 860（12.200） kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 15(2.7) kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D-638 | 15 % | |
| Impact strength of cantilever beam gap | ASTM D-256 | 14(15) kg.cm/cm | |
| tensile strength | ASTM D-638 | 500 kg/cm2 | |
| Rockwell hardness | ASTM D-785 | 116 R | |
| Flexural modulus | ASTM D-790 | 2.9 104kg/cm2 | |
| bending strength | ASTM D-790 | 860 kg/cm2 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.06(1.9) | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 1.9 g/10min | |
| ASTM D1238/ISO 1133 | 23 g/10min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | 1/16"HB | |
| Heat distortion temperature | ASTM D648/ISO 75 | 99(210) ℃（℉） | |
| ASTM D648/ISO 75 | 88(190) ℃（℉） | ||
| vicat | ASTM D1525/ISO R306 | 105(221) ℃（℉） | |
| ASTM D-1525 | 105(221) ℃(°F) | ||
| Heat distortion temperature | ASTM D-648 | 99(210)/88(190) ℃(°F) | |
| burning rate | File NO.E196075 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.