Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
melt mass-flow rate | | ASTM D1238 | 9.0 g/10min |
melt mass-flow rate | | ISO 1133 | 9.0 g/10min |
Shrinkage rate | | ASTM D955 | 2.0 % |
Shrinkage rate | | ISO 294-4 | 2.3 % |
Shrinkage rate | | ISO 294-4 | 2.4 % |
Water absorption rate | | ISO 62 | 0.54 % |
Water absorption rate | | ASTM D570 | 0.22 % |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | | ASTM D785 | 80 |
Rockwell hardness | | ISO 2039-2 | 93 |
flammability | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL 94 | HB |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Flexural modulus | | ISO 178 | 2750 Mpa |
bending strength | | ASTM D790 | 91.0 Mpa |
bending strength | | ISO 178 | 87.0 Mpa |
tensile strength | | ASTM D638 | 62.0 Mpa |
tensile strength | | ISO 527-2 | 65.0 Mpa |
elongation | | ASTM D638 | 70 % |
Tensile strain | | ISO 527-2 | 50 % |
Flexural modulus | | ASTM D790 | 2500 Mpa |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Surface Resistivity | | ASTM D257 | 1E+16 ohms |
Surface Resistivity | | IEC 60093 | 1E+16 ohms |
Volume resistivity | | ASTM D257 | 1E+14 ohms·cm |
Volume resistivity | | IEC 60093 | 1E+14 ohms·cm |
dielectric strength | | ASTM D149 | 19 KV/mm |
dielectric strength | | IEC 60243-1 | 19 KV/mm |
dielectric constant | | ASTM D150 | 3.70 |
Dissipation Factor | | ASTM D150 | 6E-03 |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | 158 °C |
Heat distortion temperature | | ASTM D648 | 110 °C |
Heat distortion temperature | | ISO 75-2/A | 95.0 °C |
vicat | | ASTM D1525 | 162 °C |
melting temperature | | ISO 11357-3 | 166 °C |
melting temperature | | | 166 °C |
Linear coefficient of thermal expansion | | ASTM D696 | 1.3E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.