Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ASTM D955 | 0.15to0.40 % |
| Water absorption rate | | ASTM D570 | 0.90 % |
| density | | ASTM D792 | 1.50 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Limiting Oxygen Index | | ASTM D2863 | 24 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| elongation | Yield | ASTM D638 | 2.5 % |
| elongation | Break | ASTM D638 | 2.5 % |
| Flexural modulus | | ASTM D790 | 7580 MPa |
| bending strength | | ASTM D790 | 190 MPa |
| tensile strength | | ASTM D638 | 128 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 85 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 1E+14 ohms·cm |
| dielectric strength | | ASTM D149 | 12 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 213 °C |
| Heat distortion temperature | | ASTM D648 | 205 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 5.5E-05 cm/cm/°C |
| RTI Elec | | UL 746 | 65.0 °C |
| RTI Elec | | UL 746 | 65.0 °C |
| RTI Elec | | UL 746 | 65.0 °C |
| RTI Imp | | UL 746 | 65.0 °C |
| RTI Imp | | UL 746 | 65.0 °C |
| RTI Imp | | UL 746 | 65.0 °C |
| RTI Str | | UL 746 | 65.0 °C |
| RTI Str | | UL 746 | 65.0 °C |
| melting temperature | | | 216 °C |
| RTI Str | | UL 746 | 65.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare