Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.73 g/cm³ |
| Water absorption rate | | ASTM D570 | 0.18 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-0 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 86.9 MPa |
| tensile strength | | ASTM D638 | 65.5 MPa |
| bending strength | | ASTM D790 | 150 MPa |
| bending strength | | ASTM D790 | 175 MPa |
| compressive strength | | ASTM D695 | 163 MPa |
| compressive strength | | ASTM D695 | 161 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 370 J/m |
| Impact strength of cantilever beam gap | | ASTM D256 | 400 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | >17 kV/mm |
| dielectric constant | | ASTM D150 | 4.28 |
| dielectric constant | | ASTM D150 | 4.07 |
| Dissipation Factor | | ASTM D150 | 0.014 |
| Dissipation Factor | | ASTM D150 | 0.014 |
| arc resistance | | ASTM D495 | 141 sec |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | | UL 746 | PLC 1 sec |
| dielectric strength | | ASTM D149 | 77500 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Elec | | UL 746 | 130 °C |
| RTI | | UL 746 | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.