Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Melt volume flow rate | | ISO1133 | 15.0 cm3/10min |
| SpiralFlow2.3 | | 内部方法 | 100 CM |
| Shrinkage rate | | ISO294-4 | 0.90 % |
| Shrinkage rate | | ISO294-4 | 0.50 % |
| HumidityAbsorption-62%RH | | ISO1110 | 1.7 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning rate 5 | | FMVSS302 | <100 mm/min |
| UL flame retardant rating | | UL94 | HB |
| Burning wire flammability index | | IEC60695-2-12 | 700 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 725 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| ReinforcementContent | | ISO1172 | 15 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/1 | 5200 Mpa |
| Tensile stress | | ISO527-2/5 | 105 Mpa |
| Tensile strain | | ISO527-2/5 | 3.3 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO179/1eU | 60 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 60 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/B | 215 °C |
| | ISO75-2/A | 192 °C |
| Melting temperature 5 | | DINEN11357-1 | 220 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices