Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 密度 | | ASTMD792 | 1.12 g/cm³ |
| 密度 | | ISO1183 | 1.12 g/cm³ |
| 熔体质量流动速率 | 220°C/10.0kg | ASTMD1238 | 25 g/10min |
| 熔体质量流动速率 | 220°C/10.0kg | ISO1133 | 24 g/10min |
| 收缩率 | MD：3.20mm | ASTMD955 | 0.30 % |
| 收缩率 | TD：3.20mm | ASTMD955 | 0.30 % |
| 收缩率 | TD:3.20mm | ISO2577 | 0.40 % |
| 收缩率 | MD:3.20mm | ISO2577 | 0.40 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 热变形温度 | 0.45MPa,Annealed,4.00mm | ISO75-2/B | 92.0 °C |
| 热变形温度 | 1.8MPa,未退火,6.40mm | ASTMD648 | 80.0 °C |
| 热变形温度 | 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 72.0 °C |
| 热变形温度 | 1.8MPa,Annealed,4.00mm | ISO75-2/A | 86.0 °C |
| 维卡软化温度 | -- | ISO306/B50 | 92.090.0 °C |
| 维卡软化温度 | -- | ISO306/B120 | 92.0 °C |
| 热变形温度 | 0.45MPa,未退火,6.40mm | ASTMD648 | 90.0 °C |
| 热变形温度 | 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 83.0 °C |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | 0.8mm | UL94 | HB |
| UL阻燃等级 | 2.0mm | UL94 | HB |
| UL阻燃等级 | 3.0mm | UL94 | HB |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 抗张强度 | 屈服 | ASTMD638 | 49.0 Mpa |
| 拉伸应力 | 屈服 | ISO527-2/50 | 52.0 Mpa |
| 抗张强度 | 断裂 | ASTMD638 | 36.3 Mpa |
| 拉伸应力 | 断裂 | ISO527-2/50 | 36.0 Mpa |
| 伸长率 | 断裂 | ASTMD638 | 18 % |
| 拉伸应变 | 断裂 | ISO527-2/50 | 22 % |
| 弯曲模量 | | ASTMD790 | 2350 Mpa |
| 弯曲模量 | | ISO178 | 2360 Mpa |
| 弯曲强度3 | | ASTMD790 | 66.7 Mpa |
| 弯曲应力 | | ISO178 | 70.0 Mpa |
| 拉伸模量 | | ASTMD638 | 2080 Mpa |
| 拉伸模量 | | ISO527-2/50 | 2500 Mpa |
| 硬度 | Test Condition | Test Method | Test Result |
|---|
| 洛氏硬度 | R级 | ASTMD785 | 114 |
| 洛氏硬度 | R级 | ISO2039-2 | 115 |
| PencilHardness | --6 | JISK5401 | F |
| PencilHardness | --7 | JISK5401 | F |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 8.0 kJ/m² |
| 悬壁梁缺口冲击强度 | 23°C,3.18mm | ASTMD256 | 78 J/m |
| 悬壁梁缺口冲击强度 | 23°C,6.35mm | ASTMD256 | 64 J/m |
| 悬壁梁缺口冲击强度5 | 23°C | ISO180/1A | 7.4 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.