Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 密度 | | ASTMD792 | 1.68 g/cm³ |
| 熔体质量流动速率 | 275°C/2.16kg | ASTMD1238 | 0.90到1.3 g/10min |
| 收缩率 | MD | ASTMD955 | 2.5 % |
| 吸水率 | Equilibrium | ASTMD570 | <0.10 % |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 抗张强度 | 断裂,23°C | ASTMD638 | 54.0 MPa |
| 伸长率 | 屈服,23°C | ASTMD638 | 5.0 % |
| 伸长率 | 断裂,23°C | ASTMD638 | 250 % |
| 弯曲模量 | 23°C | ASTMD790 | 1690 MPa |
| 摩擦系数 | 泰伯耐磨性(1000Cycles,500g,CS-17转轮) | ASTMD1894 | 5.00 mg |
| 拉伸模量 | 23°C | ASTMD638 | 1660 MPa |
| 抗张强度 | 屈服,23°C | ASTMD638 | 30.0 MPa |
| 弯曲强度 | 23°C | ASTMD790 | 47.0 MPa |
| 摩擦系数 | Itself - Dynamic | ASTMD1894 | 0.20 |
| 摩擦系数 | Itself - Static | ASTMD1894 | 0.20 |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | | UL94 | V-0 |
| 极限氧指数 | | ASTMD2863 | 52 % |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|
| 体积电阻率 | 23°C | ASTMD257 | 5.5E+16 ohms·cm |
| 介电强度 | 23°C,3.20mm | ASTMD149 | 14 kV/mm |
| 介电常数 | 23°C,1MHz | ASTMD150 | 2.57 |
| 硬度 | Test Condition | Test Method | Test Result |
|---|
| 洛氏硬度 | R-Scale | ASTMD785 | 90 |
| 肖氏硬度 | 邵氏D | ASTMD2240 | 75 |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 导热系数 | 40°C | ASTMC177 | 0.15 W/m/K |
| 结晶热 | | ASTMD3418 | 40.0 J/g |
| 热稳定性- | | TGA | 405 °C |
| 融合热量 | | ASTMD3418 | 42.0 J/g |
| 悬壁梁缺口冲击强度 | -40°C,3.20mm | ASTMD256 | 210 J/m |
| 悬壁梁缺口冲击强度 | 23°C,3.20mm | ASTMD256 | 无断裂 |
| 热变形温度 | 0.45MPa,未退火 | ASTMD648 | 90.0 °C |
| 热变形温度 | 1.8MPa,未退火 | ASTMD648 | 65.0 °C |
| 脆化温度 | | ASTMD746A | <-76.0 °C |
| 玻璃转化温度 | | DMA | 85.0 °C |
| 熔融温度 | | ASTMD3418 | 242 °C |
| 结晶峰温度 | DSC | ASTMD3418 | 222 °C |
| 线性热膨胀系数 | MD | ASTMD696 | 1E-04 cm/cm/°C |
| 比热 | 23°C | ASTMD3418 | 962 J/kg/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare