| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO1133 | 45.0 cm³/10min | |
| Shrinkage rate | ISO294-4 | 1.0 % | |
| ISO294-4 | 1.0 % | ||
| density | ISO1183 | 1.02 g/cm³ | |
| ISO1183 | 1.02 g/cm³ | ||
| Melt volume flow rate | ISO1133 | 45.0 cm³/10min | |
| Shrinkage rate | ISO294-4 | 1.0 % | |
| ISO294-4 | 1.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179/1eU | 15 kJ/m² | |
| Charpy Notched Impact Strength | ISO179/1eA | 2.3 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179/1eU | 15 kJ/m² | |
| Charpy Notched Impact Strength | ISO179/1eA | 2.3 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO527-2 | 2400 MPa | |
| Tensile stress | ISO527-2 | 26.0 MPa | |
| Tensile strain | Break | ISO527-2 | 4.7 % |
| Flexural modulus | ISO178 | 2300 MPa | |
| Bending stress | ISO178 | 43.0 MPa | |
| Fracture bending strain | ISO178 | 5.3 % | |
| Tensile modulus | ISO527-2 | 2400 MPa | |
| Tensile stress | ISO527-2 | 26.0 MPa | |
| Tensile strain | Break | ISO527-2 | 4.7 % |
| Flexural modulus | ISO178 | 2300 MPa | |
| Bending stress | ISO178 | 43.0 MPa | |
| Fracture bending strain | ISO178 | 5.3 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO75-2/A | 72.0 °C | ||
| vicat | ISO306/B | 74.0 °C | |
| ISO75-2/B | 127 °C | ||
| ISO75-2/B | 127 °C | ||
| ISO75-2/A | 72.0 °C | ||
| vicat | ISO306/B | 74.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.