Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 15 g/10min |
| melt mass-flow rate | | ISO 1133 | 0.60 g/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D2457 | 5 |
| Haze ratio | | ASTM D1003 | 80 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| PunctureResistance-EnergytoResist | | ISO 7765-2 | 150 J/cm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| coefficient of friction | | ISO 8295 | 0.40 |
| film | Test Condition | Test Method | Test Result |
|---|
| elongation | | ISO 527-3 | 650 % |
| Dart impact | | ISO 7765-1 | 150 g |
| Elmendorf tear strength | | ISO 6383-2 | 12.0 kN/m |
| Elmendorf tear strength | | ISO 6383-2 | 290.0 kN/m |
| film thickness | | | 25 µm |
| Tensile modulus | | ISO 527-3 | 500 Mpa |
| Tensile modulus | | ISO 527-3 | 650 Mpa |
| tensile strength | | ISO 527-3 | 57.0 Mpa |
| tensile strength | | ISO 527-3 | 48.0 Mpa |
| elongation | | ISO 527-3 | 400 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| melting temperature | | ISO 11357-3 | 127 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.