POM M90-44 PTM NANTONG

104

Form：Granules | Grade：Injection grade

Properties:

high viscositywear resistanttransparentHigh mobilityWeather resistancecurrency

Typical Applications:

Electrical fieldElectronic fieldHousehold appliancesHousehold appliances

Supplier(1)

Product Description

Certificates(0)

Datasheet

Alternative Model(16)

Product Description

Typical Applications:	Electrical field \| Electronic field \| Household appliances \| Household appliances
Properties:	high viscosity \| wear resistant \| transparent \| High mobility \| Weather resistance \| currency

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor	0.060MPa,0.15m/sec8	JISK7218	6500	10^-8mm³/N·m
	Wear factor	0.060MPa,0.15m/sec7	JISK7218	3500	10^-8mm³/N·m
		Wear factor	0.49MPa,0.30m/sec6	JISK7218	65	10^-8mm³/N·m
			Wear factor	0.98MPa,0.30m/sec6	JISK7218	30	10^-8mm³/N·m
				Wear factor	0.49MPa,0.30m/sec5	JISK7218	<1.0	10^-8mm³/N·m
				Wear factor	Wear factor	0.98MPa,0.30m/sec5	JISK7218	<1.0	10^-8mm³/N·m
Friction coefficient	Steel - Dynamic4	JISK7218	0.40
	Friction coefficient	Steel - Dynamic3	JISK7218	0.46
	Friction coefficient	Friction coefficient	Dynamic2	JISK7218	0.37
bending strength		ISO 178	87.0	Mpa
Bending modulus		ISO 178	2500	Mpa
Nominal tensile fracture strain		ISO 527-2	35	%
tensile strength		ISO 527-2	62.0	Mpa
Tensile modulus		ISO 527-2	2700	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	MD：23to55°C	Internal Method	1.2E-04	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	Internal Method	1.2E-04	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	95.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	0.50	%
Shrinkage rate	MD:2.00mm	ISO 294-4	2.0	%
Shrinkage rate	Shrinkage rate	TD:2.00mm	ISO 294-4	2.0	%
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	8.00	cm3/10min
melt mass-flow rate		ISO 1133	9.0	g/10min
melt mass-flow rate	melt mass-flow rate		ASTM D1238	9.0	g/10min
density		ISO 1183	1.41	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+16	ohms
Volume resistivity		IEC 60093	1E+14	ohms·cm
Dielectric strength	3.00mm	IEC 60243-1	19	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	80
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ColourNumber			CF2001/CD3068

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.