Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792 | 1.19 g/cm³ |
| melt mass-flow rate | | ASTMD1238 | 10 g/10min |
| Shrinkage rate | | 内部方法 | 0.60to0.80 % |
| Outdoor applicability | | UL746C | f1 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-2 |
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 800 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 2270 Mpa |
| tensile strength | | ASTMD638 | 62.0 Mpa |
| tensile strength | | ASTMD638 | 65.0 Mpa |
| elongation | | ASTMD638 | 6.0 % |
| elongation | | ASTMD638 | 130 % |
| Flexural modulus | | ASTMD790 | 2340 Mpa |
| bending strength | | ASTMD790 | 101 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256 | 800 J/m |
| Dart impact equipped with measuring instruments | | ASTMD3763 | 73.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Arc resistance 6 | | ASTMD495 | PLC7 |
| Compared to the Leakage Tracking Index (CTI) | | UL746 | PLC 3 |
| High arc combustion index (HAI) | | UL746 | PLC 2 |
| High Voltage Arc Traceability Rate (HVTR) | | UL746 | PLC 3 |
| Hot wire ignition (HWI) | | UL746 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTME831 | 6.7E-05 cm/cm/°C |
| | ASTME831 | 6.7E-05 cm/cm/°C |
| RTI Elec | | UL746 | 130 °C |
| RTI Imp | | UL746 | 120 °C |
| RTI Str | | UL746 | 130 °C |
| | ASTMD648 | 137 °C |
| | ASTMD648 | 126 °C |
| vicat | | ASTMD15255 | 143 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.