Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792,ISO1183 | 1.50 g/cm³ |
| melt mass-flow rate | | ISO1133 | 17 g/10min |
| Shrinkage rate | | 内部方法 | 1.5到1.8 % |
| Shrinkage rate | | 内部方法 | 1.2到1.5 % |
| Water absorption rate | | ASTMD570 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 92 |
| Rockwell hardness | R-Scale | ASTMD785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Flexural modulus | | ASTMD790 | 3000 MPa |
| Flexural modulus | | ISO178 | 3200 MPa |
| bending strength | | ASTMD790 | 96.0 MPa |
| | ASTMD1044 | 18.0 mg |
| Tensile stress | Yield | ISO527-2 | 62.0 MPa |
| Tensile stress | | ASTMD638 | 63.0 MPa |
| elongation | Break | ASTMD638,ISO527-2 | 15 % |
| Tensile modulus | | ISO527-2 | 3400 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179 | 4.0 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256 | 33 J/m |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTMD648 | 172 °C |
| Heat distortion temperature | | ISO75-2/B | 165 °C |
| Heat distortion temperature | | ASTMD648 | 140 °C |
| Heat distortion temperature | | ISO75-2/A | 110 °C |
| | ASTMD696,ISO11359-2 | 8E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.