PA+PPO(PPE)

PA+PPO(PPE) XYRON™ AG211 ASAHI JAPAN

Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179	11 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield,23°C	ISO 527-2	94.0 MPa
Tensile strain	Break,23°C	ISO 527-2	5.0 %
Bending modulus	23°C	ISO 178	3700 MPa
bending strength	23°C	ISO 178	148 MPa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD：-30to65°C	ISO 11359-2	5E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	199 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.16 g/cm³
Shrinkage rate	3.00mm	Internal Method	0.50to0.70 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity	23°C	IEC 60093	5E+15 ohms·cm
Dielectric strength	2.00mm	IEC 60243-1	27 kV/mm
Dielectric constant	100Hz	IEC 60250	3.20
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3.10
Dissipation factor	100Hz	IEC 60250	5E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.010

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.