PP S2040 SECCO SHANGHAI

Form：Granules | Grade：High melting point

Properties:

High impact resistancehigh strengthHigh temperature resistan

Typical Applications:

Fiber gradeNon-woven fabricchipTV casing

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Fiber grade \| Non-woven fabric \| chip \| TV casing
Properties:	High impact resistance \| high strength \| High temperature resistan

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
Huangdu Index		ASTM D-192563T	2	%
Cleanliness	色粒		一等品｜≤10	粒/kg树脂
Cleanliness	Cleanliness	色粒		合格品｜≤20	粒/kg树脂
fisheye	0.4mm		优等品｜≤20	个/1520cm2
	fisheye	0.4mm		一等品｜≤40	个/1520cm2
		fisheye	0.4mm		合格品｜≤60	个/1520cm2
			fisheye	0.8mm		优等品｜≤4	个/1520cm2
				fisheye	0.8mm		一等品｜≤8	个/1520cm2
				fisheye	fisheye	0.8mm		合格品｜≤16	个/1520cm2
Cleanliness	杂质		优等品｜≤20	粒/kg树脂
	Cleanliness	杂质		一等品｜≤40	粒/kg树脂
	Cleanliness	Cleanliness	杂质		合格品｜≤60	粒/kg树脂
Huangdu Index			优等品｜实测	%
	Huangdu Index			一等品｜实测	%
	Huangdu Index	Huangdu Index			合格品｜实测	%
Cleanliness	色粒		优等品｜≤5	粒/kg树脂
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D-1505	0.905	g/cm³
melt mass-flow rate		ASTM D-1238	38.0	g/10min
	melt mass-flow rate			优等品｜32.0-43.0	g/10min
		melt mass-flow rate			一等品｜32.0-43.0	g/10min
		melt mass-flow rate	melt mass-flow rate			合格品｜30.0-38.0	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Elongation at Break		ASTM D638/ISO 527	20	%
tensile strength		ASTM D638/ISO 527	34	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	94
Bending modulus		ASTM D790/ISO 178	1450	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	20	%
Bending modulus		ASTM D-790A	1450	Mpa
Impact strength of cantilever beam gap	23℃	ASTM D-256	16	J/m
tensile strength	Yield	ASTM D-638	34.0	Mpa
Rockwell hardness		ASTM D-785	94	R-Scale
elongation	Break	ASTM D-638	20	%
Impact strength of cantilever beam gap	23℃		合格品｜≥10.0	kJ/m²
Bending modulus			优等品｜实测	GPa
	Bending modulus			一等品｜实测	GPa
	Bending modulus	Bending modulus			合格品｜实测	GPa
elongation	Break		优等品｜≥20	%
	elongation	Break		一等品｜≥18	%
	elongation	elongation	Break		合格品｜≥18	%
tensile strength	Yield		优等品｜≥34.0	Mpa
	tensile strength	Yield		一等品｜≥31.0	Mpa
	tensile strength	tensile strength	Yield		合格品｜≥30.0	Mpa
Rockwell hardness			优等品｜实测	R
	Rockwell hardness			一等品｜实测	R
	Rockwell hardness	Rockwell hardness			合格品｜实测	R
Impact strength of cantilever beam gap	23℃		优等品｜≥13.5	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃		一等品｜≥10.0	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT	ASTM D648/ISO 75	99	℃（℉）
	Hot deformation temperature	0.46MPa	ASTM D-648	99	°C
		Hot deformation temperature	0.45MPa		优等品｜实测	°C
			Hot deformation temperature	0.45MPa		一等品｜实测	°C
			Hot deformation temperature	Hot deformation temperature	0.45MPa		合格品｜实测	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	0.905
melt mass-flow rate		ASTM D1238/ISO 1133	38.0	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.