'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPA AS-1133 BK324 SOLVAY USA
35
Form：Granules | Grade：Injection grade
Properties:
enhanceThermal stabilityDimensional stabilityHigh temperature resistanFiller: Glass fiber reinf33% filler by weight
Typical Applications:
Automotive componentsLaptop caseFitness equipmentFood contact partsPlumbing componentsValves/valve componentsIndustrial applicationsIndustrial componentsMetal substitutionLawn and garden equipmentPower/Other ToolsOil/Gas SuppliescurrencyParts under the hood of a carApplication in the automotive fieldFuel pipelineMachine/mechanical componentsVehicle electronicsShellThick wall accessories (components)
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Automotive components | Laptop case | Fitness equipment | Food contact parts | Plumbing components | Valves/valve components | Industrial applications | Industrial components | Metal substitution | Lawn and garden equipment | Power/Other Tools | Oil/Gas Supplies | currency | Parts under the hood of a car | Application in the automotive field | Fuel pipeline | Machine/mechanical components | Vehicle electronics | Shell | Thick wall accessories (components) |
| Properties: | enhance | Thermal stability | Dimensional stability | High temperature resistan | Filler: Glass fiber reinf | 33% filler by weight |
Certificates
No Data...
Technical Data Sheet
| optical performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| transmissivity | 1070nm:1.60mm | ASTM D1003 | >35 | % |
| 940nm:1.60mm | ASTM D1003 | >30 | % | |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 82 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 3.2mm | UL 94 | HB | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Bending modulus | ASTM D790 | 10300 | Mpa | |
| ISO 178 | 10300 | Mpa | ||
| bending strength | ISO 178 | 326 | Mpa | |
| Yield | ASTM D790 | 317 | Mpa | |
| compressive strength | ASTM D695 | 276 | Mpa | |
| shear strength | ASTM D732 | 101 | Mpa | |
| Poisson's ratio | 7.58 | 0.41 | ||
| Tensile modulus | ASTM D638 | 13100 | Mpa | |
| ISO 527-2 | 12200 | Mpa | ||
| tensile strength | Yield | ISO 527-2 | 225 | Mpa |
| Break | ASTM D638 | 221 | Mpa | |
| elongation | Break | ASTM D638 | 2.5 | % |
| Tensile strain | Break | ISO 527-2 | 3.0 | % |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45MPa,Annealed,3.18mm | ASTM D648 | 297 | °C |
| 1.8MPa,Annealed,3.18mm | ASTM D648 | 285 | °C | |
| 1.8MPa,Annealed | ISO 75-2/Af | 277 | °C | |
| Continuous use temperature | --2 | ASTM D3045 | 164 | °C |
| --3 | ASTM D3045 | 185 | °C | |
| Melting temperature | ASTM D3418 | 310 | °C | |
| ISO 11357-3 | 310 | °C | ||
| Linear coefficient of thermal expansion | MD：0to100°C | ASTME831 | 2.3E-05 | cm/cm/°C |
| MD：160to249°C | ASTME831 | 1.4E-05 | cm/cm/°C | |
| TD：0to100°C | ASTME831 | 5.9E-05 | cm/cm/°C | |
| TD：160to249°C | ASTME831 | 1.3E-04 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | MD | ASTM D955 | 0.40 | % |
| TD | ASTM D955 | 0.80 | % | |
| Water absorption rate | 24hr | ASTM D570 | 0.21 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Arc resistance | ASTM D495 | 140 | sec | |
| Compared to the anti leakage trace index | CTI | UL 746 | V | |
| Volume resistivity | ASTM D257 | 1E+16 | ohms·cm | |
| Dielectric strength | 3.17mm | ASTM D149 | 21 | KV/mm |
| Dielectric constant | 60Hz | ASTM D150 | 4.40 | |
| 1MHz | ASTM D150 | 4.20 | ||
| Dissipation factor | 60Hz | ASTM D150 | 5E-03 | |
| 1MHz | ASTM D150 | 0.017 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Scale | ASTM D785 | 125 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.