'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PPO SE1GFN2 WH50030 SABIC INNOVATIVE US
119
Form：Granules | Grade：Injection grade
Properties:
enhanceGlass fiber reinforced
Typical Applications:
Electronic communication accessoriesElectronic communication accessories
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Electronic communication accessories | Electronic communication accessories |
| Properties: | enhance | Glass fiber reinforced |
Certificates
No Data...
Technical Data Sheet
| other | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| purpose | 车辆配件 | |||
| Color | 本白色 | |||
| characteristic | 玻纤增强 | |||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 18.0 | J |
| Suspended wall beam without notch impact strength | 23°C8 | ISO 180/1U | 28 | kJ/m² |
| -30°C8 | ISO 180/1U | 27 | kJ/m² | |
| 23°C | ASTM D4812 | 520 | J/m | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 1.5 mm | UL 94 | V-1 | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| bending strength | Yield, 50.0 mm Span5 | ASTM D790 | 140 | Mpa |
| --6,7 | ISO 178 | 150 | Mpa | |
| Bending modulus | --6 | ISO 178 | 5600 | Mpa |
| 50.0 mm Span5 | ASTM D790 | 5500 | Mpa | |
| elongation | Break | ISO 527-2/50 | 2.5 | % |
| Break4 | ASTM D638 | 3.0 | % | |
| tensile strength | Break | ISO 527-2/50 | 100 | Mpa |
| Break4 | ASTM D638 | 120 | Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 6400 | Mpa |
| --3 | ASTM D638 | 7100 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 110 to 120 | °C | ||
| drying time | 3.0 to 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 30 to 70 | % | ||
| Temperature at the rear of the barrel | 265 to 315 | °C | ||
| Temperature in the middle of the barrel | 275 to 320 | °C | ||
| Temperature at the front of the material cylinder | 290 to 325 | °C | ||
| Spray nozzle temperature | 300 to 325 | °C | ||
| Processing (melt) temperature | 300 to 325 | °C | ||
| Mold temperature | 80 to 110 | °C | ||
| Back pressure | 0.300 to 0.700 | Mpa | ||
| Screw speed | 20 to 100 | rpm | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8 | ISO 75-2/Af | 133 | °C |
| Vicat softening temperature | -- | ASTM D15259 | 142 | °C |
| -- | ISO 306/B120 | 144 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 2.5E-5 | cm/cm/°C |
| Hot deformation temperature | 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 134 | °C |
| 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 142 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ISO 11359-2 | 3.0E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 7.5E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 24 hr, 23°C2 | ISO 62 | 0.040 | % |
| 24 hr, 23°C | ISO 62 | 0.11 | % | |
| Shrinkage rate | 3.20 mm，Flow | Internal Method | 0.20 - 0.50 | % |
| Melt Volume Flow Rate (MVR) | 280°C/5.0 kg | ISO 1133 | 3.00 | cm3/10min |
| melt mass-flow rate | 280°C/5.0 kg | ASTM D1238 | 3.5 | g/10 min |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | ASTM D257 | 1.3E+17 | ohms | |
| Volume resistivity | ASTM D257 | 2.0E+16 | ohms·cm | |
| Dielectric strength | 1.60 mm, in Oil | ASTM D149 | 26 | KV/mm |
| 1.50 mm, in Oil | IEC 60243-1 | 26 | KV/mm | |
| Dielectric constant | 1 MHz | ASTM D150 | 2.93 | |
| 1 MHz | IEC 60250 | 2.90 | ||
| Dissipation factor | 1 MHz | ASTM D150 | 3.4E-3 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.