Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTM D792 | 1.04 g/cm³ |
| thickness | | | 127.0to330.2 µm |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ASTM D785 | 110 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 60.7 MPa |
| Tensile modulus | | ASTM D638 | 2410 MPa |
| tensile strength | | ASTM D638 | 35.9 MPa |
| elongation | | ASTM D638 | 4.0 % |
| Flexural modulus | | ASTM D790 | 2320 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256A | 140 J/m |
| Suspended wall beam without notch impact strength | | ASTM D256 | 280 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTM D257 | 5.0E+13到4.0E+14 ohms |
| dielectric strength | | ASTM D149 | 2.8to15 kV/mm |
| dielectric constant | | ASTM D150 | 2.70to2.90 |
| Dissipation Factor | | ASTM D150 | 4.9E-3到5.2E-3 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 95.6 °C |
| Heat distortion temperature | | ASTM D648 | 82.2 °C |
| Glass Transition Temperature | | DSC | 108 °C |
| vicat | | ASTM D15256 | 98.9 °C |
| Linear coefficient of thermal expansion | | ASTME831 | 8.8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | ASTME831 | 8.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.