Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| colour | | | Amber |
| density | Pot Life | | 20 min |
| colour | | | Black |
| density | | | 1.01 g/cm³ |
| density | | | 1.16 g/cm³ |
| density | | | 0.40到1.0 Pa·s |
| density | | | 2.0 hr |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | | 7E-03 |
| Supporting hardness | | | 85 |
| LapShearStrength | | | 11.7 MPa |
| | | 3.65 |
| Volume resistivity | | | >3.0E+13 ohms·cm |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| | | 按重量计算的混合比:100 |
| | | 按重量计算的混合比:68 |
| | | 52 wk |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | | | <5.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| WeightLossonHeating | | | 1.1 % |
| WeightLossonHeating | | | 3.5 % |
| DegradationTemperature | | TGA | 365 °C |
| Shear Strength | | | 23.4 MPa |
| Operating | | | -55到200 °C |
| Operating | | | -55到300 °C |
| Operating | | | 2.26 GPa |
| WeightLossonHeating | | | 0.29 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | >40.0 °C |
| | | 5.5E-05 cm/cm/°C |
| | | 1.9E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.