Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ISO 1133 | 6.0 cm3/10min |
| Water absorption rate | | ISO 62 | 1.9 % |
| Melt volume flow rate | | ISO 1133 | 6.00 cm3/10min |
| Water absorption rate | | ISO 62 | 1.9 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Flammability level | | UL 94 | V-2 |
| Flammability level | | UL 94 | V-2 |
| Limiting Oxygen Index | | ISO 4589-2 | 25 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 1420 Mpa |
| Tensile stress | | ISO 527-2 | 41 Mpa |
| Tensile strain | | ISO 527-2 | 5.0 % |
| elongation | | ISO 527-2 | ＞50 % |
| tensile strength | | ISO 527-2 | 41.0 Mpa |
| Tensile strain | | ISO 527-2 | 5.0 % |
| Nominal tensile fracture strain | | ISO 527-2 | > 50 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | -- |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | -- |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | -- KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2 | 145 °C |
| Heat distortion temperature | | ISO 75-2 | 50 °C |
| vicat | | ISO 306 | 160 °C |
| melting temperature | | ISO 11357-3 | 189 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 0.000085 cm/cm/℃ |
| UL flame retardant rating | | ISO 1210 | V-2 |
| Limiting Oxygen Index | | ISO 4589-2 | 25 % |
| Heat distortion temperature | | ISO 75-2/B | 145 °C |
| Heat distortion temperature | | ISO 75-2/A | 50.0 °C |
| vicat | | ISO 306/B50 | 160 °C |
| melting temperature | | ISO 11357-3 | 189 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 8.5E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.