PPS A310MB7 TORAY JAPAN

Form：Granules | Grade：Injection grade

Properties:

Flame retardantGlass fiber reinforcedMineral reinforcementHigh rigidityhigh strengthHigh temperature resistan

Typical Applications:

Fiber grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Fiber grade
Properties:	Flame retardant \| Glass fiber reinforced \| Mineral reinforcement \| High rigidity \| high strength \| High temperature resistan

Certificates

No Data...

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D-570	0.02	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ASTM D-790	200	Mpa
Elongation at Break		ASTM D-732	60
limiting pv value		东丽法	815	KJ/m
Impact strength of cantilever beam gap	Notched23℃	ASTM D-256	90	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Unnotched23℃	ASTM D-256	20	KJ/m
abrasion		ASTM D-1044	70	mg/1000回
tensile strength		ASTM D-638	140	Mpa
Friction coefficient	对钢	ASTM D-1894	0.30
tensile strength		ASTM D-638	1.2	%
Shore hardness		ASTM D-785	123	洛氏
bending strength		ASTM D-790	17.6	GPa
tensile strength		ASTM D638/ISO 527	141(MPa)	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	123
bending strength		ASTM D790/ISO 178	240(MPa)	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.82MPa	ASTM D-648	>260	°C
Linear coefficient of thermal expansion	Flow	ASTM D-696	1.6
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	垂重方向	ASTM D-696	2.4
Melting temperature		DSC	278	°C
Combustibility		UL -94	V-0
Combustibility (rate)		UL 94	V-0
Melting temperature			278	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	Flow	东丽法	0.15	%
Shrinkage rate	Shrinkage rate	垂重方向	东丽法	0.55	%
	320℃,98MPa,1mm厚，Flow长	东丽法	90
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		ASTM D-149	15	MV/m
Inherent resistance of volume		ASTM D-257	10	Ω.m
Arc resistance	W电极	ASTM D-495	182	秒
Induced positive connection	10	ASTM D-150	0.002
Dielectric constant	10	ASTM D-150	5.8

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.