PC 925-701 SABIC INNOVATIVE NANSHA

Form：Granules | Grade：Injection grade

Properties:

Flame retardantBromine freecurrency

Typical Applications:

Plastic bagLighting applicationsElectrical fieldElectronic fieldArchitectural application fieldElectrical applianceslens

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Plastic bag \| Lighting applications \| Electrical field \| Electronic field \| Architectural application field \| Electrical appliances \| lens
Properties:	Flame retardant \| Bromine free \| currency

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	73.0	J
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning wire flammability index	1.6mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0mm	IEC 60695-2-13	800	°C
UL flame retardant rating	0.8mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	1.1mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Break	ASTM D638	130	%
Bending modulus	50.0mmSpan	ASTM D790	2340	Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	101	Mpa
Tensile modulus		ASTM D638	2270	Mpa
tensile strength	Yield	ASTM D638	62.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	65.0	Mpa
elongation	Yield	ASTM D638	6.0	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	137	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	126	°C
Vicat softening temperature		ASTM D15255	143	°C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6.7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	6.7E-05	cm/cm/°C
RTI Elec		UL 746	130	°C
RTI Imp		UL 746	120	°C
RTI Str		UL 746	130	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2kg	ASTM D1238	14	g/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.60-0.80	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Arc resistance		ASTM D495	PLC7
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 4
Hot wire ignition	HWI	UL 746	PLC 2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.