PA12 Grilamid® L25W40X
232
- Properties:High impact resistancehigh viscosity
- Usages:Automotive sectorConsumer goods sectorPneumatic applicationsIndustrial applicationsHydraulic applications
Compare
View PricesTechnical Data Sheet
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.02 g/cm | |
| Water absorption rate | DIN 53495 | 1.4 % | |
| DIN 53495 | 0.7 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation at break | ASTM D412/ISO 527 | >50 % | |
| Tensile modulus | ASTM D412/ISO 527 | 360 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D412/ISO 527 | 20 % | |
| Impact strength of cantilever beam gap | ISO 180/IA | 无断裂 kj/cm | |
| elongation at break | ISO 527 | 200-300 % | |
| Shore hardness | IOS 2039-1 | 30 Mpa | |
| elongation at yield | ISO 527 | 30 % | |
| Impact strength of cantilever beam gap | ISO 180/IC | 无断裂 KJ/m | |
| Tensile modulus | ISO 527 | 360 Mpa | |
| Impact strength of cantilever beam gap | ISO 180/IA | 13 kj/cm | |
| tensile strength | ISO 527 | 40 Mpa | |
| ISO 527 | 25 Mpa | ||
| Impact strength of cantilever beam gap | ISO 180/IC | 无断裂 KJ/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 10^11 Ω |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.02 kg·cm/cm(J/M)ft·lb/in | |
| Water absorption rate | ASTM D570/ISO 62 | 1.4 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648/ISO 75 | 45 ℃（℉） | |
| melting temperature | 173 ℃（℉） | ||
| Heat distortion temperature | ISO 75 | 95 °C | |
| ISO 75 | 44 °C | ||
| melting temperature | ISO 3146-C | 173 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.