Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.24 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 1.0 % |
| Shrinkage rate | | ISO 294-4 | 0.50 % |
| Water absorption rate | | ISO 62 | 1.0 % |
| Water absorption rate | | ISO 62 | 2.2 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| Burning wire flammability index | | IEC 60695-2-12 | 675 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 675 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 675 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 700 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 700 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 700 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ISO 178 | 170 MPa |
| Tensile modulus | | ISO 527-2 | 6600 MPa |
| tensile strength | | ISO 527-2 | 120 MPa |
| Tensile strain | | ISO 527-2 | 3.0 % |
| Flexural modulus | | ISO 178 | 5900 MPa |
| Poisson's ratio | | ISO 527-2 | 0.40 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 6.6 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 6.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179 | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 32 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179 | 39 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180 | 5.7 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Hot wire ignition (HWI) | | UL 746 | PLC 4 |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | | UL 746 | PLC 4 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 1 |
| Volume resistivity | | IEC 60093 | 1E+13 ohms·cm |
| dielectric strength | | IEC 60243 | 20 kV/mm |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| RTI Imp | | UL 746 | 120 °C |
| RTI Imp | | UL 746 | 120 °C |
| RTI Str | | UL 746 | 125 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/B | 258 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 241 °C |
| melting temperature | | ISO 11357-3 | 260 °C |
| | ISO 11359-2 | 3E-05 cm/cm/°C |
| | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| RTI Elec | | UL 746 | 140 °C |
| RTI Elec | | UL 746 | 140 °C |
| RTI Str | | UL 746 | 140 °C |
| RTI Str | | UL 746 | 140 °C |
| RTI Elec | | UL 746 | 140 °C |
| RTI Imp | | UL 746 | 120 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare