PC 103R-111 SABIC INNOVATIVE SPAIN

Form：Granules | Grade：Injection grade

Properties:

transparentUV resistanceWeather resistance

Typical Applications:

CastersOutdoor applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Casters \| Outdoor applications
Properties:	transparent \| UV resistance \| Weather resistance

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity	2540 μm	ASTM D1003	1.0	%
transmissivity	2540 μm	ASTM D1003	88.0	%
Refractive index		ASTM D542	1.586
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200	J/m
Dart impact	23°C	ASTM D3029	169	J
Impact strength of cantilever beam gap		ASTM D1822	546	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.76 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield	ASTM D638	62.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	65.0	Mpa
elongation	Yield	ASTM D638	7.0	%
elongation	elongation	Break	ASTM D638	110	%
Bending modulus	50.0 mm Span	ASTM D790	2340	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	93.0	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
injection	Test Condition	Test Method	Test Result	Test Unit
Spray nozzle temperature			305 to 325	°C
Processing (melt) temperature			310 to 330	°C
Mold temperature			80 to 115	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.025 to 0.076	mm
Temperature at the front of the material cylinder			310 to 330	°C
Temperature in the middle of the barrel			300 to 320	°C
Temperature at the rear of the barrel			290 to 310	°C
Suggested injection volume			40 to 60	%
Suggested maximum moisture content			0.020	%
drying time			3.0 to 4.0	hr
drying temperature			120	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	132	°C
Vicat softening temperature		ASTM D15255	154	°C
Linear coefficient of thermal expansion	-40 to 95°C，Flow	ASTM E831	6.8E-5	cm/cm/°C
specific heat		ASTM C351	1250	J/kg/°C
thermal conductivity		ASTM C177	0.19	W/m/K
RTI Elec		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI		UL 746	130	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Specific volume		ASTM D792	0.830	cm³/g
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	7.0	g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Water absorption rate	24 hr	ASTM D570	0.15	%
	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35	%
	Water absorption rate	Water absorption rate	Equilibrium, 100°C	ASTM D570	0.58	%
Outdoor applicability		UL 746C	f1
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Hot wire ignition		UL 746	PLC 4
High voltage arc tracing rate		UL 746	PLC 2
High arc combustion index		UL 746	PLC 1
Compared to the anti leakage trace index		UL 746	PLC 2
Dissipation factor	1 MHz	ASTM D150	0.010
	Dissipation factor	60 Hz	ASTM D150	9.0E-4
	Dissipation factor	Dissipation factor	50 Hz	ASTM D150	9.0E-4
Dielectric constant	1 MHz	ASTM D150	2.96
	Dielectric constant	50 kHz	ASTM D150	3.17
	Dielectric constant	Dielectric constant	60 Hz	ASTM D150	3.17
Dielectric strength	3.20 mm, in Air	ASTM D149	15	KV/mm
Volume resistivity		ASTM D257	> 1.0E+17	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ASTM D785	70
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	118

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.