Technical Data Sheet
| 基本性能 | Test Condition | Test Method | Test Result |
|---|
| 熔体质量流动速率 | 220°C/10.0kg | ASTMD1238 | 23 g/10min |
| 熔体体积流动速率 | 220°C/10.0kg | ISO1133 | 23.0 cm3/10min |
| 收缩率 | | ISO294-4 | 0.40to0.70 % |
| 熔体质量流动速率 | 220℃,10kg | ASTM D-1238 | 28 g/10min |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 热变形温度 | 1.8MPa,未退火 | ISO75-2/A | 80.0 °C |
| 热变形温度 | 1.8MPa,退火 | ISO75-2/A | 97.0 °C |
| 维卡软化温度 | | ASTMD15256 | 105 °C |
| 维卡软化温度 | -- | ISO306/A50 | 105 °C |
| 维卡软化温度 | -- | ISO306/B50 | 94.0 °C |
| 线性热膨胀系数 | MD | ISO11359-2 | 9E-05 cm/cm/°C |
| 热变形温度 | Annealed | ASTMD648 | 95 °C |
| 热变形温度 | Unannealed | ASTMD648 | 85 °C |
| 软化点 | | ASTM D-1525 | 105 °C |
| 热变形温度 | | ASTM D648/ISO 75 | 95 ℃（℉） |
| 热变形温度 | | ASTM D648/ISO 75 | 85 ℃（℉） |
| 维卡软化温度 | | ASTM D1525/ISO R306 | 105 ℃（℉） |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | 1.5mm | UL94 | HB |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 弯曲模量 | | ISO178 | 2200 Mpa |
| 弯曲强度 | | ASTMD790 | 63.3 Mpa |
| 弯曲应力5 | | ISO178 | 67.0 Mpa |
| 抗张强度 | 屈服 | ASTMD638 | 43.0 Mpa |
| 拉伸应力 | 屈服 | ISO527-2/50 | 46.0 Mpa |
| 拉伸应力 | 断裂 | ISO527-2/50 | 33.0 Mpa |
| 伸长率 | 断裂 | ASTMD638 | 55 % |
| 拉伸应变 | 断裂 | ISO527-2/50 | 20 % |
| 弯曲模量 | | ASTMD790 | 2160 Mpa |
| 引张强度 | | ASTM D-638 | 420 kg/cm |
| 弯曲强度 | | ASTM D-790 | 550 kg/cm |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 15 kg.cm/cm |
| IZOD 缺口冲击强度 | | ASTM D256/ISO 179 | 10 kg·cm/cm(J/M)ft·lb/in |
| IZOD 缺口冲击强度 | | ASTM D256/ISO 179 | 15 kg·cm/cm(J/M)ft·lb/in |
| 拉伸强度 | | ASTM D638/ISO 527 | 440 kg/cm²(MPa)[Lb/in²] |
| 弯曲强度 | | ASTM D790/ISO 178 | 650 kg/cm²(MPa)[Lb/in²] |
| 硬度 | Test Condition | Test Method | Test Result |
|---|
| 洛氏硬度 | R级 | ASTMD785 | 105 |
| 物性性能 | Test Condition | Test Method | Test Result |
|---|
| 密度 | | ASTM D792/ISO 1183 | 1.07 |
| 熔体质量流动速率 | | ASTM D1238/ISO 1133 | 28 g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare
View Prices