PBT VX5022-7001 SABIC INNOVATIVE US

Form：Granules | Grade：Enhanced level

Properties:

High mobilityHigh crystallinityAging resistanceFiller: Glass fiber reinf20%Filler by weight

Typical Applications:

engineering application Automotive componentsElectronic and electrical components

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	engineering application \| Automotive components \| Electronic and electrical components
Properties:	High mobility \| High crystallinity \| Aging resistance \| Filler: Glass fiber reinf \| 20% \| Filler by weight

Certificates

No Data...

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt viscosity	260°C,1500sec^-1	ISO 11443	215	Pa·s
impact performance	Test Condition	Test Method	Test Result	Test Unit
-30°C		ISO 179/1eA	5.5	kJ/m²
-30°C	-30°C		ISO 179/2C	9.0	kJ/m²
23°C		ISO 179/1eA	6.5	kJ/m²
23°C	23°C		ISO 179/2C	9.0	kJ/m²
-30°C		ISO 179/1eU	40	kJ/m²
-30°C	-30°C		ISO 179/2U	50	kJ/m²
23°C		ISO 179/1eU	40	kJ/m²
23°C	23°C		ISO 179/2U	55	kJ/m²
-30°C		ASTM D256	80	J/m
0°C		ASTM D256	80	J/m
23°C		ASTM D256	80	J/m
Dart impact	23°C,TotalEnergy	ASTM D3763	65.0	J
23°C		ISO 180/1U	40	kJ/m²
-30°C		ISO 180/1U	35	kJ/m²
23°C		ASTM D4812	650	J/m
23°C	23°C		ISO 180/1A	7.0	kJ/m²
-30°C		ASTM D4812	650	J/m
0°C		ISO 180/1A	7.0	kJ/m²
-30°C		ISO 180/1A	6.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Extreme Oxygen Index		ISO 4589-2	23	%
Burning wire flammability index	2.00mm	IEC 60695-2-12	850	°C
Burning wire flammability index	Burning wire flammability index	1.00mm	IEC 60695-2-12	750	°C
UL flame retardant rating	1.60mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Fracture bending strain		ISO 178	3.0	%
Yield, 50.0mm span		ASTM D790	145	Mpa
--10		ISO 178	150	Mpa
--9		ISO 178	6300	Mpa
50.0mm span		ASTM D790	5800	Mpa
crack		ISO 527-2/5	3.0	%
crack	crack		ASTM D638	3.0	%
yield		ISO 527-2/5	3.0	%
	yield		ASTM D638	3.0	%
		yield		ASTM D638	125	Mpa
		yield	yield		ISO 527-2/5	110	Mpa
--3		ASTM D638	7300	Mpa
crack		ASTM D638	125	Mpa
crack	crack		ISO 527-2/5	110	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Horizontal: -40 to 40 ° C	Across Flow, -40to40℃	ASTME831	1E-04	cm/cm/°C
Horizontal: -40 to 40 ° C	Horizontal: -40 to 40 ° C	Across Flow, -40to40℃	ISO 11359-2	6.9E-05	cm/cm/°C
Horizontal: 23 to 60 ° C	Across Flow, 23to60℃	ISO 11359-2	1E-04	cm/cm/°C
Horizontal: 23 to 80 ° C	Across Flow, 23to80℃	ISO 11359-2	1E-04	cm/cm/°C
Horizontal: 23 to 150 ° C	Across Flow, 23to150℃	ISO 11359-2	1.1E-04	cm/cm/°C
Flow: -40 to 40 ° C		ISO 11359-2	2.5E-05	cm/cm/°C
Flow: 23 to 60 ° C	23to60℃	ISO 11359-2	4E-05	cm/cm/°C
Flow: 23 to 80 ° C	23to80℃	ISO 11359-2	4E-05	cm/cm/°C
Flow: 23 to 150 ° C	23to150℃	ISO 11359-2	2.4E-05	cm/cm/°C
1.8MPa, unannealed, 3.20mm		ASTM D648	120	°C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	120	°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Flow: -40 to 40 ° C		ASTME831	4E-05	cm/cm/°C
0.45MPa, unannealed, 64.0mm span		ISO 75-2/Bf	180	°C
0.45MPa, unannealed, 3.20mm		ASTM D648	180	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Saturation,23°C	ISO 62	0.10	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.060	%
melt mass-flow rate	250°C/2.16kg	ASTM D1238	16	g/10min
Shrinkage rate	MD1	Internal Method	0.30-0.80	%
melt mass-flow rate	266°C/5.0kg	ASTM D1238	50	g/10min
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	28.0	cm3/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	13.0	cm3/10min
density		ASTMD792	1.39	g/cm³
melt mass-flow rate	265°C/5.0kg	ASTM D1238	50	g/10min
Shrinkage rate	TD2	Internal Method	0.50-0.90	%
Shrinkage rate	Shrinkage rate	MD:3.20mm	Internal Method	0.30-0.50	%
Melt Volume Flow Rate (MVR)	265°C/5.0kg	ISO 1133	40.0	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Hot wire ignition	HWI	UL 746	PLC 0
High arc combustion index	HAI	UL 746	PLC 0
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 4
Compared to the anti leakage trace index	Compared to the anti leakage trace index	--	IEC 60112	PLC 3
100Hz	100Hz	IEC 60250	1E-03
60Hz	60Hz	IEC 60250	1E-03
60Hz	60Hz	60Hz	IEC 60250	3.10
100Hz	100Hz	IEC 60250	3.30
1MHz	1MHz	ASTMD150	0.014
50Hz	50Hz	IEC 60250	1E-03
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		ASTMD257	>1.0E+15	ohms·cm
0.800mm,inOil		ASTM D149	31	KV/mm
1.60mm,inOil		ASTM D149	28	KV/mm
3.20mm, inoil		ASTM D149	16	KV/mm
0.800mm, in oil		IEC 60243-1	31	KV/mm
50Hz	50Hz	IEC 60250	3.10
3.20mm, in oil		IEC 60243-1	16	KV/mm
1MHz	1MHz	ASTMD150	3.30
1.60mm, in oil		IEC 60243-1	28	KV/mm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale	ISO 2039-2	122
Ball Pressure Test	H358/30	ISO 2039-1	205	Mpa
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
Filling material		ASTM D229	20	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PBT VX5022-7001 SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index