Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 0.930 g/cm³ |
| melt mass-flow rate | | ISO1133 | 15 g/10min |
| density | | ISO 1183 | 0.930 g/cm³ |
| | ISO 1133 | 15 g/10 min |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| UL flame retardant rating | | UL94 | V-0 |
| Burning wire flammability index | | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC60695-2-13 | 775 °C |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 775 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO527-2/5 | 1000 MPa |
| Tensile stress | | ISO527-2/5 | 100 MPa |
| Tensile strain | | ISO527-2/5 | 20 % |
| Tensile modulus | | ISO 527-2/5 | 1000 MPa |
| Tensile stress | | ISO 527-2/5 | 100 MPa |
| Tensile strain | | ISO 527-2/5 | 20 % |
| Impact strength of cantilever beam gap | | ISO 180/1A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO 180/1A | 60 kJ/m² |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ISO180/1A | 10 kJ/m² |
| Impact strength of cantilever beam gap | | ISO180/1A | 60 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1E+15 ohms |
| Volume resistivity | | IEC60093 | 1E+15 ohms·cm |
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/A | 50.0 °C |
| melting temperature | | ISO11357 | 165 °C |
| melting temperature | | ISO 11357 | 165 °C |
| | ISO 75-2/A | 50 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.