AES DIALAC® KD100W
904
- Certificates:UL
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | ISO 1133 | 90.0 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 0.60-0.80 % | |
| Melt volume flow rate | ISO 1133 | 90.0 cm3/10min | |
| Shrinkage rate | ISO 294-4 | 0.60 - 0.80 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 104 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-2 | |
| UL 94 | V-2 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2280 Mpa | |
| tensile strength | ISO 527-2 | 43.0 Mpa | |
| Flexural modulus | ISO 178 | 2550 Mpa | |
| bending strength | ISO 178 | 68.0 Mpa | |
| Rockwell hardness | ISO 2039-2 | 104 R 计秤 | |
| Tensile modulus | ISO 527-2 | 2280 Mpa | |
| tensile strength | ISO 527-2 | 43.0 Mpa | |
| Flexural modulus | ISO 178 | 2550 Mpa | |
| bending strength | ISO 178 | 68.0 Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 2.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Af | 72.0 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 8E-05 cm/cm/°C | |
| Heat distortion temperature | ISO 75-2/Af | 72.0 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 0.000080 cm/cm/℃ | |
| UL flame retardant rating | UL 94 | V-2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.