Technical Data Sheet
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Color | | | Clear/Transparent |
| density | | | 1.08 g/cm³ |
| Viscosity | | | 0.15to0.25 Pa·s |
| Cured Properties | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | | 74 |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| shelf-life | | | 52 wk |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| refractive index | | | 1.473 |
| refractive index | | | 1.504 |
| refractive index | | | >98.0 % |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| weight loss on heating | | | 1.2 % |
| weight loss on heating | | | 1.9 % |
| DegradationTemperature | | | 385 °C |
| Shear Strength | | | 7.03 MPa |
| operate temperature | | | -55-200 °C |
| weight loss on heating | | | 0.79 % |
| operate temperature | | | -55-300 °C |
| operate temperature | | | 1.73 GPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Glass Transition Temperature | | | >70.0 °C |
| Linear coefficient of thermal expansion | | | 6.9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | | | 1.7E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.