Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ASTMD792,ISO1183 | 1.30到1.32 g/cm³ |
| melt mass-flow rate | | ASTMD1238,ISO1133 | 12 g/10min |
| Shrinkage rate | | ASTMD955 | 0.30到0.40 % |
| Shrinkage rate | | ASTMD955 | 0.60到0.80 % |
| Water absorption rate | | ASTMD570,ISO62 | 1.0 % |
| Water absorption rate | Saturation | ASTMD570 | 6.5 % |
| Water absorption rate | | ISO62 | 6.5 % |
| GranuleHumidity | | 内部方法 | <0.10 % |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale | ASTMD785 | 120 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Hot filament ignition temperature | | IEC60695-2-13 | 750 °C |
| Limiting Oxygen Index | | ASTMD2863 | 24 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638,ISO527-2 | 8300 MPa |
| tensile strength | Break | ASTMD638,ISO527-2 | 160 MPa |
| elongation | Break | ASTMD638,ISO527-2 | 3.5 % |
| Flexural modulus | | ASTMD790,ISO178 | 8000 MPa |
| Bending stress | | ISO178 | 240 MPa |
| Bending stress | Break | ASTMD790 | 240 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO179,ASTMD256 | 7.5 kJ/m² |
| Impact strength of cantilever beam gap | | ASTMD256,ISO180 | 100 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ASTMD257 | 7E+15 ohms·cm |
| CTI | | IEC60112 | 550 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Continuous use temperature | | IEC60216 | 180 °C |
| vicat | | ISO306/B50,ASTMD15257 | 210 °C |
| melting temperature | | ASTMD211,ISO121 | 222 °C |
| | ASTMD696 | 3.5E-05 cm/cm/°C |
| Continuous use temperature | | IEC60216 | 140 °C |
| | ASTMD648,ISO75-2/A | 200 °C |
| Continuous use temperature | | IEC60216 | 100 °C |
| Continuous use temperature | | IEC60216 | 130 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.