Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTM D570 | 0.30 % |
| Shrinkage rate | | ASTM D955 | 0.70 % |
| melt mass-flow rate | | ASTM D1238 | 6.5 g/10min |
| density | | ASTM D792 | 1.24 g/cm³ |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Hot filament ignition temperature | | IEC 60695-2-13 | 850 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 875 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | | UL 94 | V-0 |
| UL flame retardant rating | | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D1822 | 420 kJ/m² |
| Impact strength of cantilever beam gap | | ASTM D256 | 69 J/m |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | | ASTM D790 | 106 Mpa |
| Flexural modulus | | ASTM D790 | 2690 Mpa |
| elongation | | ASTM D638 | 50to100 % |
| tensile strength | | ASTM D638 | 70.3 Mpa |
| Tensile modulus | | ASTM D638 | 2480 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric constant | | ASTM D150 | 3.02 |
| Dissipation Factor | | ASTM D150 | 7E-04 |
| dielectric constant | | ASTM D150 | 3.04 |
| dielectric constant | | ASTM D150 | 3.03 |
| dielectric strength | | ASTM D149 | 17 KV/mm |
| Volume resistivity | | ASTM D257 | 3E+16 ohms·cm |
| Dissipation Factor | | ASTM D150 | 6E-03 |
| Dissipation Factor | | ASTM D150 | 1E-03 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ASTM D696 | 5.6E-05 cm/cm/°C |
| Heat distortion temperature | | ASTM D648 | 174 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.