PA612 Zytel® 153HSL-NC010 DUPONT USA

420

Properties:
Mineral reinforcement
Thermal stability
Usages:
Engineering accessories
Automotive Applications
Certificates:
UL
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD	ISO294-4	1.4	%
Shrinkage rate	Shrinkage rate	MD	ISO294-4	1.3	%
Water absorption rate	饱和,23°C,2.00mm	ISO62	3.0	%
Water absorption rate	Water absorption rate	平衡,23°C,2.00mm,50%RH	ISO62	1.3	%
Stickiness number	96%H2SO4	ISO307	115	cm³/g

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ISO527-2	2400	Mpa
tensile strength	屈服	ISO527-2	62.0	Mpa
elongation	屈服	ISO527-2	4.4	%
Nominal tensile fracture strain		ISO527-2	30	%
Bending modulus		ISO178	2100	Mpa
abrasion resistance		ISO4649	6.00	mm³
Impact strength of simply supported beam without notch	-30°C	ISO179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179/1eU	NoBreak

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,未退火	ISO75-2/B	135	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,未退火	ISO75-2/A	62.0	°C
vicat softening point		ISO306/B50	180	°C
Melting temperature		ISO11357-3	218	°C
Linear coefficient of thermal expansion	MD：--	ISO11359-2	1.2E-04	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO11359-2	9E-05	cm/cm/°C
		Linear coefficient of thermal expansion	MD：55to160°C	ISO11359-2	1.7E-04	cm/cm/°C
			Linear coefficient of thermal expansion	TD：--	ISO11359-2	1.2E-04	cm/cm/°C
				Linear coefficient of thermal expansion	TD：-40to23°C	ISO11359-2	9E-05	cm/cm/°C
					Linear coefficient of thermal expansion	TD：55to160°C	ISO11359-2	1.8E-04	cm/cm/°C
					Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO11359-2	7E-08	m²/s

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	--	ohms
Volume resistivity		IEC60093	1E+15	ohms·cm
Dielectric strength		IEC60243-1	30	KV/mm
Relative permittivity	100Hz	IEC60250	3.60
Relative permittivity	Relative permittivity	1MHz	IEC60250	3.20
Dissipation factor	100Hz	IEC60250	0.014
Dissipation factor	Dissipation factor	1MHz	IEC60250	0.016
Leakage Trace Index		IEC60112	600	V

film	Test Condition	Test Method	Test Result	Unit
Tensile strain MD	Yield	ISO527-3	4.4	%

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate	1.00mm	ISO3795	<100	mm/min
UL flame retardant rating	0.9mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	0.9mm	IEC60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	1.5mm	IEC60695-11-10,-20	HB
Extreme Oxygen Index		ISO4589-2	27	%
FMVSS flammability		FMVSS302	B

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.