PA46 Stanyl® TW278F10

Properties:
Thermal stability
Usages:
Automotive Applications
Home appliance components
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ISO 294-4	0.90 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.40 %
Water absorption rate		ISO 62	1.6 %

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	16000 Mpa
	Tensile modulus		ISO 527-2	8300 Mpa
	Tensile modulus	Tensile modulus		ISO 527-2	7600 Mpa
Tensile stress		ISO 527-2	235 Mpa
	Tensile stress		ISO 527-2	120 Mpa
	Tensile stress	Tensile stress		ISO 527-2	105 Mpa
Tensile strain		ISO 527-2	2.2 %
	Tensile strain		ISO 527-2	3.4 %
	Tensile strain	Tensile strain		ISO 527-2	3.5 %
Flexural modulus		ISO 178	12500 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch		ISO 179/1eU	35 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179/1eU	55 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/B	288 °C
Heat distortion temperature	Heat distortion temperature		ISO 75-2/A	285 °C
Melting temperature 2		ISO 11357-3	290 °C
		ISO 11359-2	3.0E-5 cm/cm/°C
			ISO 11359-2	3.0E-5 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.