PA6 8202 BASF KOREA

Form：Granules | Grade：Injection grade

Properties:

Thermal stabilityhigh strengthOil resistant

Typical Applications:

HelmetAutomotive ApplicationsEngine parts

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Helmet \| Automotive Applications \| Engine parts
Properties:	Thermal stability \| high strength \| Oil resistant

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C	Internal Method	142	J
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179	51	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.71mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-2
		UL flame retardant rating	3.0mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating	6.0mm	UL 94	V-2
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ISO 178	85.0	Mpa
bending strength	bending strength	121°C	ASTM D790	17.0	Mpa
tensile strength	Yield,150°C	ISO 527-2	20.0	Mpa
tensile strength	tensile strength	Break,23°C	ASTM D638	75.0	Mpa
elongation	Yield,23°C	ASTM D638	4.0	%
Bending modulus	-40°C	ASTM D790	3010	Mpa
	Bending modulus	23°C	ASTM D790	2830	Mpa
		Bending modulus	65°C	ASTM D790	500	Mpa
			Bending modulus	90°C	ASTM D790	350	Mpa
				Bending modulus	121°C	ASTM D790	305	Mpa
				Bending modulus	Bending modulus	23°C	ISO 178	2400	Mpa
bending strength	-40°C	ASTM D790	170	Mpa
	bending strength	23°C	ASTM D790	108	Mpa
		bending strength	65°C	ASTM D790	30.0	Mpa
		bending strength	bending strength	90°C	ASTM D790	20.0	Mpa
Tensile modulus	23°C	ISO 527-2	2700	Mpa
	Tensile modulus	80°C	ISO 527-2	485	Mpa
		Tensile modulus	120°C	ISO 527-2	360	Mpa
		Tensile modulus	Tensile modulus	150°C	ISO 527-2	290	Mpa
tensile strength	Yield,-40°C	ASTM D638	126	Mpa
	tensile strength	Yield,23°C	ASTM D638	78.0	Mpa
		tensile strength	Yield,80°C	ASTM D638	35.0	Mpa
			tensile strength	Yield,121°C	ASTM D638	25.0	Mpa
				tensile strength	Yield,-40°C	ISO 527-2	126	Mpa
					tensile strength	Yield,23°C	ISO 527-2	78.0	Mpa
						tensile strength	Yield,80°C	ISO 527-2	35.0	Mpa
						tensile strength	tensile strength	Yield,120°C	ISO 527-2	25.0	Mpa
elongation	Yield,80°C	ASTM D638	42	%
elongation	elongation	Yield,121°C	ASTM D638	36	%
Tensile strain	Yield,23°C	ISO 527-2	4.0	%
elongation	Break,23°C	ASTM D638	55	%
Nominal tensile fracture strain	23°C	ISO 527-2	25	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	178	°C
RTI Str	6.0mm	UL 746	85.0	°C
	RTI Str	3.0mm	UL 746	85.0	°C
	RTI Str	RTI Str	1.5mm	UL 746	85.0	°C
RTI Imp	6.0mm	UL 746	75.0	°C
	RTI Imp	3.0mm	UL 746	75.0	°C
	RTI Imp	RTI Imp	1.5mm	UL 746	75.0	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	150	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	65.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	60.0	°C
Melting temperature		ASTM D3418	220	°C
Melting temperature	Melting temperature		ISO 3146	220	°C
Linear coefficient of thermal expansion	MD	ASTME831	8.3E-05	cm/cm/°C
RTI Elec	0.71mm	UL 746	125	°C
	RTI Elec	1.5mm	UL 746	125	°C
		RTI Elec	3.0mm	UL 746	125	°C
		RTI Elec	RTI Elec	6.0mm	UL 746	125	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.7	%
	Water absorption rate	Equilibrium,50%RH	ASTM D570	2.7	%
		Water absorption rate	Saturation,23°C	ISO 62	9.5	%
			Water absorption rate	Saturation	ASTM D570	9.5	%
				Water absorption rate	23°C,24hr	ISO 62	1.6	%
				Water absorption rate	Water absorption rate	24hr	ASTM D570	1.6	%
Shrinkage rate	MD：3.18mm		1.2	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	100Hz	IEC 60250	3.50
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3.30
Dissipation factor	100Hz	IEC 60250	0.010
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.020
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dielectric strength		IEC 60243-1	37	KV/mm
Dielectric strength	Dielectric strength	1.50mm	ASTM D149	22	KV/mm
Volume resistivity		IEC 60093	>1.0E+13	ohms·cm
Volume resistivity	Volume resistivity	1.50mm	ASTM D257	>1.0E+13	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	119

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.